We are engaged in the Supplying and Trading of Ethylene Vinyl Acetate (EVA). Ethylene Vinyl Acetate (EVA) is a polymer widely used as an encapsulant between the glass cover of a solar module and the glass cover of the solar cells within the module. Ethylene Vinyl Acetate (EVA) can be obtained at affordable rates from clients.
| PROPERTY | UNIT | VALUE | TEST METHOD |
|---|---|---|---|
|
MELT FLOW INDEX (2.16 kg/190oC) |
g/10min |
2.3 |
ASTM D 1238 |
|
DENSITY |
g/cm3 |
0.941 |
ASTM D 1505 |
|
TENSILE STRENGTH AT YIELD |
MPa |
4.5 |
ASTM D 638 |
|
TENSILE STRENGTH AT BREAK |
MPa |
24 |
ASTM D 638 |
|
ULTIMATE ELONGATION |
% |
820 |
ASTM D 638 |
|
HARDNESS SHORE - D |
-- |
37 |
DIN 53505 |
|
VICAT SOFTENING TEMPERATURE |
oC |
62 |
ASTM D 1525 |
|
VA CONTENT |
% |
18 |
TPI METHOD |
| PROPERTY | MELT FLOW INDEX (2.16kg/190oC) | DENSITY | TENSILE STRENGTH AT YIELD | TENSILE STRENGTH AT BREAK | ULTIMATE ELONGATION | HARDNESS SHORE-D | VICAT SOFTENING TEMPERATURE | VA CONTENT |
|---|---|---|---|---|---|---|---|---|
|
TEST METHOD UNIT |
ASTM D1238 (g/10 min) |
ASTM D1505 (g/cm3) |
ASTM D638 (MPa) |
ASTM D638 (MPa) |
ASTM D638 (%) |
DIN 53505 (-) |
ASTM D1525 (oC) |
TPI METHOD (%) |
|
N8036 |
1.7 |
0.937 |
4.9 |
23.5 |
780 |
38 |
68 |
15 |
|
N 8038 F |
2.3 |
ko |
0.941 |
4.5 |
24 |
820 |
37 |
62 |
|
N 8038 |
2.3 |
0.941 |
4.5 |
24 |
820 |
37 |
37 |
15 |
|
N 8045 |
2.5 |
0.947 |
3.5 |
30 |
830 |
36 |
58 |
22 |
|
MV 1055 |
8 |
0.953 |
2.5 |
23 |
840 |
28 |
49 |
28 |
|
SV 1055 |
20 |
0.952 |
- |
17 |
860 |
25 |
48 |
28 |
|
TV 1055 |
40 |
0.952 |
- |
10 |
840 |
27 |
47 |
28 |